| NO | Property | Units | Typical vaule |
| 1 | Aluminum coil | mm | 0.20+/-0.01 |
| Copolymer coat | mm | 0.058+/-0.013 | |
| Total | mm | 0.32+/-0.042 | |
| 2 | Color | Nature | |
| 3 | Peel strength | N/cm | min 6.13 |
| Between Aluminum and Copolymer | |||
| 4 | Tensile Strength | MPA | min 65 |
| 5 | Elongation | % | min 15 |
| 6 | Filler/Flooding Resistance | No delamination | |
| 68±1ºC,168 h | |||
| 7 | Heat seal strength | N/cm | min 17.5 |
| 8 | Cutting strength | No damage | |
| 9 | Dielectric strength (DC2KV 1 min) | Without breakdown | |
| 10 | Corrosion Resistance | Grade | min 7 |
| 0.1mol/L NaOH 480 h |
| NO | Property | Units | Typical vaule |
| 1 | Aluminum coil | mm | 0.20+/-0.01 |
| Copolymer coat | mm | 0.058+/-0.013 | |
| Total | mm | 0.32+/-0.042 | |
| 2 | Color | Nature | |
| 3 | Peel strength | N/cm | min 6.13 |
| Between Aluminum and Copolymer | |||
| 4 | Tensile Strength | MPA | min 65 |
| 5 | Elongation | % | min 15 |
| 6 | Filler/Flooding Resistance | No delamination | |
| 68±1ºC,168 h | |||
| 7 | Heat seal strength | N/cm | min 17.5 |
| 8 | Cutting strength | No damage | |
| 9 | Dielectric strength (DC2KV 1 min) | Without breakdown | |
| 10 | Corrosion Resistance | Grade | min 7 |
| 0.1mol/L NaOH 480 h |