| Property | PTFE | Reinforced PTFE |
| Density | 2.2 g/cm3 ± 0.1 | 2.2 g/cm3 ± 0.1 |
| Tensile Strength | 15.0～18.0 Mpa /2175～ 2610 Psi | > 18.0 Mpa / 2600 Psi |
| Compressibility | ≥ 15% | 9～15% |
| Recovery | > 30% | > 35% |
| Sealability | ≤ 0.06 ml/min | ≤ 0.06 ml/min |
| Temp. Range | Temp. Range -200 ～ 260℃ /-382 ～ 500℉ | Temp. Range -200 ～ 260℃ /-382 ～ 500℉ |
| Max. Continuous Pressure | 1.03 Mpa / 149 Psi | 4.0 Mpa / 580 Psi |
| Stress Relaxaton Rate | / | ≤ 70% |
| Elongation at Break | / | ≥210% |
| Thickness | 1/16"(1.5mm),1/8"(3.0mm) | |
| Sheet Size | 1.0mX1.0m,1.5mX1.5m |
| Property | PTFE | Reinforced PTFE |
| Density | 2.2 g/cm3 ± 0.1 | 2.2 g/cm3 ± 0.1 |
| Tensile Strength | 15.0～18.0 Mpa /2175～ 2610 Psi | > 18.0 Mpa / 2600 Psi |
| Compressibility | ≥ 15% | 9～15% |
| Recovery | > 30% | > 35% |
| Sealability | ≤ 0.06 ml/min | ≤ 0.06 ml/min |
| Temp. Range | Temp. Range -200 ～ 260℃ /-382 ～ 500℉ | Temp. Range -200 ～ 260℃ /-382 ～ 500℉ |
| Max. Continuous Pressure | 1.03 Mpa / 149 Psi | 4.0 Mpa / 580 Psi |
| Stress Relaxaton Rate | / | ≤ 70% |
| Elongation at Break | / | ≥210% |
| Thickness | 1/16"(1.5mm),1/8"(3.0mm) | |
| Sheet Size | 1.0mX1.0m,1.5mX1.5m |